UJI KUALITAS CAMPURAN ABU SEKAM PADI DAN SERBUK ABU ECENG GONDOK SEBAGAI BAHAN AGREGAT HALUS PEMBUATAN BATAKO

  • Ernawati Ernawati Kampus II UIN Alauddin Makassar Jl. Muh. Yasin Limpo No. 36 Samata, Gowa
    (ID)
  • Muh. Said L. Universitas Islam Negeri Alauddin Makassar
    (ID)

Abstract

This study aimed to compare the effect of adding aggregate rice husk ash and ash hyacinth of compressive strength and water absorption in the brick material, as well as great knowing the composition of the addition of rice husk ash and ash water hyacinth on the brick material. This study uses a beam-shaped test samples with a length of 15 cm, a width of 8 cm and 6 cm high with the addition of fine aggregate composition that varies the normal, 10%, 20%, 30% and 40%. Brick-making with a mixture of sand, cement, water and a mixture of rice husk ash and ash water hyacinth. The drying process is naturally carried out for 28 days. Testing the compressive strength of concrete blocks using forney engine while testing for absorption of water soaking for 24 hours. Based on test results obtained by each parameter is for the compressive strength with samples of rice husk ash (SP) is minimum 24.87 kg / cm2 and the maximum is 98.04 cm / kg2, for ash water hyacinth (EG) as a minimum 65.41 kg / cm2 and the maximum is 111.69 kg / cm2 and the mixing of the two materials (SP + EG) as a minimum 43.53 kg / cm2 and the maximum is 66.56 kg / cm2 (according to ISO standards 03-0349-1989); the value of water absorption of rice husk ash (SP) is minimum 7.30% and maximum 19.32%, for the ash water hyacinth (EG) is minimum 1.21% and maximum 1.33% and for the mixing of the two materials (SP + EG) at a minimum of 8.05 and maximum 13.71 (according to the standard SNI03-0349-1989).

 

Keywords: Brick, Compressive strength, Water absorption, Rice hulls, Water hyacin.

Downloads

Download data is not yet available.

References

Abdullah Bin Muhammad Alu Syaikh, Tafsir Ibnu Katsir Jilid 2. Jakarta: Pustaka Imam Asy-Syafi’i, 2008.

Alfredo, Marchin. Studi Kuat Tekan Beton Normal Mutu Sedang Dengan Campuran Abu Sekam Padi (RHA) dan Limbah Adukan Beton (CSW). Universitas Indonesia. 2012.

Anggoro, Wahyu. Karakteristik batako Ringan Dengan Campuran Limbah Styrofoam ditinjau dari Densitas, Kuat Tekan dan Daya Serap Air. Universitas Negeri semarang. 2014.

Anam, Saiful, dkk. Pemanfaatan Serbuk Eceng Gondok Sebagai Campuran Beton Mutu Tinggi. Universitas Wahid Hasyim semarang. 2015.

Anver, Suardi. Uji Kuat Tekan dan Serapan Air Pada Pembuatan Batako Dengan Bahan Tambahan Mill (Serbuk Batu Putih) Gunung Kidul Yokyakarta. Universitas Atma Jaya Yokyakarta. 2013.

Bahreisy, Said. 1988. Tafsir Ibnu Katsir. Jilid I. Kuala Lumpur Victory Agencia.

Bakri. Komponen Kimia dan fisik Abu Sekam Padi Sebagai SCM Untuk Pembuatan Komposit Semen. Jurnal Perennial, 5 (1): 9-14. 2008.

Depertemen Agama RI. 2002. Al-Qur’an Al-Karim dan Terjemahnya. Semarang: PT. Karya Toha Putra

Departemen Pekerjaan Umum. 1982. Persyaratan Umum Bahan Bangunan di Indonesia. Bandung.

Departemen Pekerjaan Umum. 1989, SNI 03-0349-1989. Bata Beton untuk Pasangan Dinding. Balitbang Jakarta.

Firdaus, Apriyadi. Proses Pembuatan Semen Pada PT. Holcim Indonesia tbk. Cilegon: Universitas Sultan Agung Tirtayasa. 2007.

Giancoli C. Douglas. 2001. Fisika Kelima Edisi 1. Jakarta: Erlangga.

Hermanto, Dony, dkk. Kuat Tekan Batako Dengan Variasi Bahan Tambah Serat Ijuk. e-jurnal Matriks Teknik Sipil/September 2014/491.

Harun, Mellisa. Studi Kelayakan Kualitas Batako Hasil Produksi Industri Kecil di Kota Palu. Media Litbang Sulteng IV (2): 75-82. Desember 2011.

httpwww.materipertanian.comklasifikasi-dan-ciri-ciri-morfologi-ecenggondok.html.

httpsayunasti.files.wordpress.com2014031751195620x310.jpg

httpsbatakojogja.files.wordpress.com201204img0368a.jpg

Marsudi. Pengembangan tanah Blenket Asal Desa Jatipohon Kabupaten Grobogan Sebagai Bahan Pembuatan Batako. Jurnal Teknis Vol. 5 No.1 April 2010: 16.

Nasrudin, Muhammad. Analisis Sifat Mekanik dan Struktur Mikro Batako Dengan Campuran Abu Terbang Batubara. Universitas Islam Negeri Sunan Kalijaga Yokyakarta. 2014.

Santoso, Henry Hermawan. Pemanfaatan Limbah Kertas HVS Sebagai Bahan Campuran Batako Dengan Alat Tekan Manual. Fakultas Teknik. Universitas Negeri Semarang. 2013.

SNI 03-0349-1989. Bata Beton Untuk Pasangan Dinding. Badan Standar Nasional. ICS 91.100.30. Uji Sifat Kimia PT. Hakiki. Juni 2009.

Published
2017-06-30
How to Cite
Ernawati, E., & Said L., M. (2017). UJI KUALITAS CAMPURAN ABU SEKAM PADI DAN SERBUK ABU ECENG GONDOK SEBAGAI BAHAN AGREGAT HALUS PEMBUATAN BATAKO. JFT: Jurnal Fisika Dan Terapannya, 4(1), 1-8. https://doi.org/10.24252/jft.v4i1.15668
Section
Artikel
Abstract viewed = 278 times