ANALISIS LAJU KOROSI BESI BETON DENGAN MEDIUM TANAH RAWA

  • Rahmaniah Rahmaniah Universitas Islam Negeri Alauddin Makassar
    (ID)
  • Nurul Amalia Universitas Islam Negeri Alauddin Makassar
  • Ihsan Ihsan Universitas Islam Negeri Alauddin Makassar

Abstract

The research on corrosion rate analysis of concrete iron with swamp
soil medium has been conducted. The aims of this study were to determine the
corrosion rate and the types of corrosion that occurred in concrete iron with
swamp soil medium. The methods of this study are Weight Loss method, Atomic
Absorption Spectroscopy (AAS) test, and Scanning Electron Microscope-Energy
Dispersion X-Ray (SEM-EDX). This study used a different immersion time
variant, such as 20 days, 40 days, 65 days, and without medium for 65 days. The
concrete iron used in this study is concrete U-24 or plain concrete iron 10. The
corrosion rate that occurs in iron concrete with swamp soil medium at 20 days
immersion is 20977.5868 mmpy, 40 days immersion is 17721.9174 mmpy, 65
days immersion is 16932. 9071 and 65 days without a medium are 3023.3793
mmpy. The more time, the rate of corrosion become more slowly due to the
influence of corrosion products that have occurred. The corrosion rate without the
medium is slower than the corrosion rate with the medium. The types of corrosion
that occurs in concrete iron with swamp soil medium are crevice corrosion and
pitting corrosion.

Downloads

Download data is not yet available.

Author Biography

Rahmaniah Rahmaniah, Universitas Islam Negeri Alauddin Makassar
Physics departement

References

Afandi, Yudha Kurniawan, dkk. (2015). Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating. Jurnal Teknik. Vol 4 (1): 1-5.

ASTM Internasional. (2004). ASTM G31-72: Standar Practice for Laboratory Immersion Corrosion Testing Of Metals. United State

Besi. “Ensiklopedai Bebas”. http://budisma.net/2015/03/pengertian-ciri-dan-sifat- besi.html ( diakses 10 Juli 2018)

Besi beton. “Ensiklopedai Bebas”. https://www.besibeton.net/products/besi- beton-polos-sni-10mm/(diakses 10 Juli 2018)

Besi Beton. “Ensiklopedai Bebas”. https://nikifour.co.id/mengenal-besi-beton-dan- memilih-kualitas-terbaik/ (diakses 09 Juli 2018)

Chang, Raymond. (2005). Kimia Dasar Edisi Ketiga Jilid 2. Jakarta : Erlangga. Fontana, Mars Guy. 1986. Corrosion Engineering. Singapore: McGraw-Hill BookCo.

Gapsari, Femiana. 2017. Pengantar Korosi. Malang : UBMedia

Haryono, G. 2010. Ekstrak Bahan Alam sebagai Inhibitor Korosi. Jurnal. Vol. 16 (1): 1-6.

J.,Trethewey, KR. 1991. Korosi . Jakarta : PT. Gramedia Pustaka Utama.

Kementrian Agama R.I., 2014. Mushaf An-Nazhif Edisi Terjemahan Tajwid. Surakarta: PT. Tiga Serangkai.

Khiatuddin, Maulida. 2003. Melestarikan Sumberdaya air dengan Teknologi Rawa Buatan. Yogyakarta:Gadjah Mada University Press

Knofel, Dietbert. 1978. Corrosion Of Building Material . United States : Van Nostrand Reinhold Company Chamberlain.

Notohadiprawiro, Tejoyuwono. 2006. Tanah dan Lingkungan. Repro:Ilmu Tanah Universitas Gaja Mada

Prameswari, Bunga. 2008. Studi Efektifitas Lapis Galvanis Terhdapa Ketahanan Korosi Pipa Baja ASTM A53 Di Dalam Tanah (Underground Pipe). Skripsi Fakultas Teknik Unvesitas Indonesia. Jakarta

Permadi, Lingga Bayu dan Aisyah Endah Palupi. 2014. Analisa Laju Korosi Pada Baja Karbon Ringan (Mild Steel) Dengan Perlakuan Bending Pada Media Pengkorosi Larutan. JTM. Vol 3 No (1): 49-54.

Priyotomo, Gadang. 2018. Kamus Saku Korosi Material. Banten : Puspiptek. Rawa. “Ensiklopedai Bebas”. http://www.g excess.com/pengertian-rawa-atau-tanah-rawa.html (diakses 11 Juli 2018)

Republik Indonesia. 1991. “Peraturan Pemerintah No.27 Tahun 1991 tentang Rawa”. Sekretaris Negara. Jakarta Sam,Alimuddin. Analisa Kecepatan Korosi Pipa Galvanis Pada Tanah Dengan Tingkat Kehalusan yang Berbeda. Jurnal Teknik Mesin. Vol.3 No.4 (2005)

Shihab, M.Quraish. 2003. Tafsir Al-Mishbah Vol 14. Jakarata : Lentera

Hati.

Shihab, M.Quraish. 2004. Tafsir Al-Mishbah Vol 8. Jakarata : Lentera Hati.

Shihab, M. Quraish. 2009.Tafsir Al Mishbah Vol 9. Jakarta : Lentera Hati.

Sidiq, M.Fajar. 2013. Analisa Korosi dan Pengendaliannya. Jurnal Foundry Vol. 3 No. (1):25 -30.

Sudarti, Tety. 2014. Mekanisme Inhibisi Korosi Baja Karbon Dalam Lingkungan Airs Sadah. Jurnal. Vol 1 No. (2):16-31.

Syabatini, Annisa. 2009. Analisis Cd dan Cu dengan metode Spektrofotometri Serapan Atom. Jurnal AAS

Tanah Rawa. “Ensiklopedai Bebas”. https://geografi.sobatmateri.com/pengertian- ciri-jenis-dan-manfaat-rawa/ (diakses 11 Juli 2018)

Tanah Rawa. “Ensiklopedai Bebas”. https://portal-ilmu.com/pengertian-jenis-dan- manfaat-rawa/ (diakses 11 Juli 2018)

Uhlig, H.H. W.R. Revie. 2000. Uhlig’s Corrosion Handbook, John Wiley and Sons p.582. New York.

Wahjudi, Didik dan Roche Alimin. 2000. Rekayasa Mutu Besi Beton dengan Metode Taguchi. Jurnal Teknik Mesin Vol. 2 (2): 102 – 108

Widharto, Sri. 1999. Karat dan Pencegahannya. Jakarta: PT Pradnya

Paramita. Wirarna, dkk. 2015. Analisa Kandungan Timbal pada Buah Apel (Pyrus Malus, L) yang dipajangkan dipinggir Jalankota Palu menggunakan Metode Spektrofotometri Serapan Atom . Jurnal of Natural Science Vol 4(1) : 32 – 45.

Published
2019-12-30
How to Cite
Rahmaniah, R., Amalia, N., & Ihsan, I. (2019). ANALISIS LAJU KOROSI BESI BETON DENGAN MEDIUM TANAH RAWA. JFT: Jurnal Fisika Dan Terapannya, 6(2), 121-132. https://doi.org/10.24252/jft.v6i2.11724
Section
Artikel
Abstract viewed = 667 times

Most read articles by the same author(s)

> >>