PENGARUH KOMPOSISI DAN UKURAN PARTIKEL TERHADAP KUALITAS BRIKET KULIT DURIAN DAN TEMPURUNG KELAPA

  • Muh. Ashar Alauddin State islamic University, Makassar
    (ID)
  • Sahara Sahara Universitas Islam Negeri Alauddin Makassar
  • Hernawati Hernawati Universitas Islam Negeri Alauddin Makassar
    (ID)

Abstract

Research has been carried out on the utilization of durian rind and coconut shell waste by turning it into bio briquette. This study aims to determine the amount of heat, water content and duration of combustion in order to obtain the best quality. Samples were made with the composition of durian rind, coconut shell, and tapioca flour as an adhesive. Each sample was carbonized with a combustion drum and furnished at a temperature of 2500C, then grinding, sifting, and molding were carried out. The composition variations used are (20:80)%, (40:60)%, (60:40)%, and (80:20)% with particle sizes of 100 mesh and 170 mesh, the adhesive mass used is 3 gr. The results of the study, testing the calorific value using the bomb calorimeter obtained the best quality in the composition (80:20)% with a size of 100 mesh of 6482,76 cal/gr, the results of testing the moisture content using an 1050C oven obtained the best quality in the composition (80:20)% with a 100 mesh size of 6,77% and the longest burning test with the longest burning duration in composition (20:80)% with a 170 mesh size of 211,8 minutes/gr.

Downloads

Download data is not yet available.

References

Badan Pusat Statistik, 2018. Statistik Lingkungan Hidup Indonesia. ISSN: 0216-6224. Jakarta.

Badan Standarisasi Nasional, 2000. Wood Charcoal Briquette, SNI 01-6235-2000, Jakarta. Dikutif dari jurnal Sainstech Politeknik Indonesia

Bakhtiar, Y. 2010. Dikutif dari jurnal Teknik Kimia. Muhammad Faizal dkk. 2014. Pengaruh Komposisi Arang Dan Perekat Terhadap Kualitas Biobriket Dari Kayu Karet. Universitas Sriwijaya.

Budi NW dkk., 2016. Penggunaan Tongkol Jagung Dalam Meningkatkan Nilai Kalor Pada Briket. Jurnal Integrasi Proses vol 6 Vol (1): 16-21.

Budi, Esmar. 2011. Pemanfaatan briket arang tempurung kelapa sebagai bahan bakar pengganti.Jurnal fisika, 12(2). Djoehana, Setyamidjaja, 1995. Bertanam Kelapa. Penerbit Kanisius: Yogyakarta. Fikri Utama, Tahnpa Tahun. Mesin Briket Batu Bara, Mesin Tempurung Kelapa Arang Kayu. Diundunh28/09/2019: http://www.trijayasantika.com/msn/msnbriket.htm.

Fuat, M. 2008. Pemanfaatan Limbah Cangkang Kopi Untuk Pembuatan Briket Biorang Menggunakan Perekat Amilium. Palembang dikutif dari Jurnal Teknik Kimia,

Hendra dan Winarni, 2003. Sifat-Sifat Fisis dan Kimia Briket Arang Campuran Limbah Kayu Gergaji Dan Sabetan Kayu. Buletin Penelitian Hasil Hutan. 21(3): 211-226. Pusat Penelitian dan Pengembangan Hasil Hutan Bogor.

Hikmat Basyir dkk. 2016. Tafsir Muyassar 2 Memahami Al Quran dengan Terjemahan dan Penafsiran Paling Mudah. Darul Haq. Jakarta

Husnah Nyimas, 2016. Pengaruh komposisi dan suhu karbonisasi pembuatan briket dari campuran serbuk gergaji kayu, tongkol jagung dan kulit durian terhadap nilai kalor. Universitas Muhammadiyah Palembang.

Indah Suryani dkk. 2012. Pembuatan Briket Arang Dari Campuran Buah Bintaro Dan Tempurung Kelpa Menggunakan Perekat Amilium.

Jamilatun S., 2008. Sifat – Sifat Penyalaan dan Pembakaran Briket Biomassa, briket batu bara dan Arang Kayu. Jurnal Rekayasa proses.,Vol.2, no. 2, 2008.

Kemas R dan Joko S, 2016. Perbandingan pembakaran priolisis dan karbonisasi pada biomassa kulit durian terhadap nilai kalor. Universitas Muhammadiyah Metro. Lampung

Moeskin Rosdiana dkk, 2017. Pembuatan Briket Bioarang Dari Campuran Limbah Tempurung Kelapa Sawit Dan Cangkang Biji Karet. Jurusan Teknik Kimia. Universitas Sriwijaya .

Monica CR dkk, 2012. Pembuatan Briket Arang dari Limbah Organik Dengan Menggunakan Variasi Komposisi dan Ukuran Bahan. Prosiding Seminar Nasional Kimia dan Pendidikan Kimia,UNS surakarta.

Muhammad Irfan dkk, 2019. Perbandingan Timbulan Sampah Laut Dan Daratan Di Lokasi Wisata Berbasis Konservasi. Jurnal ArahaN, Vol. VIII No. 2 Des 2019: 172-178. P-ISSN 2301-7163, e-ISSN 2621-9638.

Nurmawati dkk, 2018. Tingkat Kerentanan Wilayah Pesisir Kota Makassar Terhadap Pencemaran Sampah.Jurnal Ilmiah Wawasan pendidikan Vol. 4, No. 3, Agustus 2018.

Nyimas Husnah F, 2016. Pengaruh Komposisi dan Suhu Karbonisasi Pembuatan Briket dari Campuran Serbuk Gergaji Kayu, Tongkol Jagung dan Kulit Burian Terhadap Nilai Kalor. Universitas Muhammadiyah Palembang.

Paisal dan Karyani, M.Said. 2014. Analisa Kualitas Briket Arang Kulit Durian Dengan Campuran Kulit Pisang Pada Berbagai Komposisi Sebagai Bahan Bakar Alternatife. Jurusan Teknik Mesin. Ambon: Poltek

Rhiduan Kemas dan Joko Suranto, 2016. Perbandingan Pembakaran Pirolisi Dan Karbonisasi Pada Biomassa Kulit Durian Terhadap Nilai Kalor. Jurnal Teknik Mesin Univ. Muhammadiyah Metro. Lampung.

Rusdianto, Adi. 2011. Pemanfaatan Serbuk Tempurung Kelapa Sebagai Campuran Gipsum Plafon dengan Bahan Pengikat Lateks Akrilik. Progr Pascasarjana Fakultas MIPA Universitas Sumatera Utara: Medan.

Saleh, A. dkk. 2017. Analisis Kualitas Briket Serbuk Gergaji Kayu Dengan Penambahan Tempurung Kelapa Sebagai Bahan Alternatife. Jurusan Kimia, Fakultas Sains dan Teknologi. UIN Alauddin Makassar.

Sobir, Ph.D dan Rodame M. Napitupulu, S.P.,M.M. 2015 Berkebun Durian Unggul. Penebar Swadaya: Jakarta

Sumartono, 1981. Kelapa. CV. Bumirestu: Jakarta

Surakarta,Sudiro dan Sigit Suroto. 2014. Pengaruh Komposisi Dan Ukuran Serbuk Briket Yang Terbuat Dari Batubara Dan Jerami Padi Terhadap Karakteristik Pembakaran.

Suryani I, dkk. 2012. Pembuatan Briket Arang Dari Campuran Buah Bintaro Dan Tempurung Kelapa Menggunakan Perekat Amilium. Dikutif Jurnal Teknik Kimia, Moeskin R, dkk. 2017. Pembuatan Briket Bioarang Dari Campuran Limbah Tempurung Kelapa Sawit Dan Cangkang Biji Karet. Jurusan Teknik Kimia. Universitas Sriwijaya

Tim Nasional, 2007; Tirona et al, 2011; Syamsirol et al, 2007). Dikutif dari Jurnal Teknologi Industri Pertanian, Wahidin Nuriana Dkk. 2013. Karakteristik biobriket kulit durian sebagai bahan alternatife terbarukan.

Violet, Hatta. 2007. Dikutif dari jurnal Aplikasi Fisika Volume 13 No.1.

Hasan, E. Dkk. 2017. Analisis Proximate Dan Nilai Kalor Briket Hybrid (Brown Coal-Kulit Durian) Dengan Perekat Liquid Volatile (LVM) Yang Di Preparasi Dengan Metode Pirolisis. Universitas Haluleo. Kendari.

Yeni Ruslinda dkk, 2017. Karakteristik Briket Dari Komposit Samapah Buah, Sampah Plastic High Density Polyethylene (HDPE) Dan Tempurung Kelapa Sebagai Bahan Bakar Alternatif Rumah Tangga. Universitas Andalas Jurnal Presipitasi vol. 14 No. 1 ISSN 1907-187X.

Zaenul Ahmad. A, 2017. Pengaruh Variasi Jumlah Perekat Tepung Tapioca Terhadap Karakteristik Briket Arang Tempurung Kelapa. Universitas Negeri Semarang.

Published
2020-11-03
How to Cite
Ashar, M., Sahara, S., & Hernawati, H. (2020). PENGARUH KOMPOSISI DAN UKURAN PARTIKEL TERHADAP KUALITAS BRIKET KULIT DURIAN DAN TEMPURUNG KELAPA. JFT: Jurnal Fisika Dan Terapannya, 7(1), 33-43. https://doi.org/10.24252/jft.v7i1.13964
Section
Artikel
Abstract viewed = 1067 times

Most read articles by the same author(s)

> >>